CrN/NbN coatings deposited by HIPIMS: A preliminary study of erosion–corrosion performance

PURANDARE, Yashodhan, EHIASARIAN, Arutiun, STACK, M.M. and HOVSEPIAN, Papken (2010). CrN/NbN coatings deposited by HIPIMS: A preliminary study of erosion–corrosion performance. Surface and Coatings Technology, 204 (8), 1158-1162.

Full text not available from this repository.

Abstract

Nanoscale CrN/NbN multilayer PVD coatings have exhibited resistance to erosion–corrosion. However growth defects (under dense structures and droplets) in the coating produced by some deposition technologies reduce the ability to offer combined erosion–corrosion resistance. In this work a novel High Power Impulse Magnetron Sputtering (HIPIMS) technique has been utilised to pretreat substrates and deposit dense nanoscale CrN/NbN PVD coatings (HIPIMS–HIPIMS technique). This new technique, rich with metal ion plasma, deposits very dense structures and offers virtually defect free coatings (free of droplets as observed in cathodic arc technique and under-dense structures observed in standard dc sputtering). Plasma diagnostic studies revealed a high metal ion-to-gas ion ratio (Cr:Ar) of 3:1 for HIPIMS pretreatment conditions with the detection of 14% Cr2+ and 1% Cr3+ ions and Js of 155 mAcm− 2. For deposition conditions the metal ion-to-gas ratio was approximately 1:4 which is significantly higher compared to DC at 1:30. Characterisation results revealed a high adhesion of LC 80 N, high hardness of 34 GPa and Young's modulus of 381 GPa. Low friction coefficient (0.46) and dry sliding wear coefficient, KC (1.22 × 10− 15 m3Nm− 1) were recorded. The effect of deposition technique (droplet defect and intergranular void free coatings) on erosion–corrosion resistance of CrN/NbN coatings has been evaluated by subjecting the coatings to a slurry impingement (Na2CO3 + NaHCO3 buffer solution with Al2O3 particles of size 500–700 µm) at 90° impact angle with a velocity of 4 ms− 1. Experiments have been carried at − 1000 mV, + 300 mV and + 700 mV representing 3 different corrosion conditions.

Item Type:	Article
Research Institute, Centre or Group - Does NOT include content added after October 2018:	Materials and Engineering Research Institute > Advanced Coatings and Composites Research Centre > Nanotechnology Centre for PVD Research
Identification Number:	https://doi.org/10.1016/j.surfcoat.2009.11.006
Page Range:	1158-1162
Depositing User:	Helen Garner
Date Deposited:	03 Jan 2012 16:48
Last Modified:	18 Mar 2021 10:15
URI:	https://shura.shu.ac.uk/id/eprint/4239

Actions (login required)

View Item

Downloads

Publication Metrics