LUO, Quanshun, MEI, Haijuan, KITCHEN, Matthew, GAO, Yubi and BOWEN, Leon (2021). Effect of short-term low-temperature austempering on the microstructure and abrasive wear of medium-carbon low-alloy steel. Metals and Materials International.
|
PDF
Luo_EffectShort-Term(VoR).pdf - Published Version Creative Commons Attribution. Download (5MB) | Preview |
Abstract
Nano-bainitic steels have attracted great attention for good wear resistance. In this research, a medium-carbon low-alloyed steel was austempered at a low temperature close to its martensite-start temperature for various times to obtain mixed microstructure of nano-bainite, martensite and retained austenite. The austempered samples were characterised comprehensively by field-emission SEM and quantitative XRD. Its two-body abrasive wear property was evaluated by sliding on a SiC abrasive disc. The results revealed the formation of initial nano-width carbide-free bainitic ferrite (BF) after austempering by 10 minutes, whereas the BF size and amount both increased with the austempering time. The austempered samples exhibited wear coefficients lower than the quenched martensitic sample by up to 50%. SEM and TEM observations showed wear mechanisms of micro-cutting and ploughing deformation, including the formation of a nano-laminate top layer and bending deformation in the subsurface multiphase microstructure. The decreased wear loss was attributed to the role of retained austenite in the increased plasticity.
Item Type: | Article |
---|---|
Uncontrolled Keywords: | Materials; 0912 Materials Engineering |
Identification Number: | https://doi.org/10.1007/s12540-020-00957-6 |
SWORD Depositor: | Symplectic Elements |
Depositing User: | Symplectic Elements |
Date Deposited: | 18 Dec 2020 12:44 |
Last Modified: | 18 May 2021 10:15 |
URI: | https://shura.shu.ac.uk/id/eprint/27846 |
Actions (login required)
View Item |
Downloads
Downloads per month over past year