LIAO, Jinfa, WANG, Hang and CHEN, Tzu-Yu (2018). Experimental investigation and thermodynamic calculation of Ni–Al–La ternary system in nickel-rich region: A new intermetallic compound Ni2AlLa. Materials, 11 (12), p. 2396. [Article]
Documents
23551:523981
PDF
Chen_Experimental_Investigation_(VoR).pdf - Published Version
Available under License Creative Commons Attribution.
Chen_Experimental_Investigation_(VoR).pdf - Published Version
Available under License Creative Commons Attribution.
Download (5MB) | Preview
Abstract
The phase equilibrium of the Ni–Al–La ternary system in a nickel-rich region was observed at 800 °C and 1000 °C using scanning electron microscopy backscattered electron imaging, energy dispersive X-ray spectrometry and X-ray diffractometry. The solubility of Al in the Ni5La phase was remeasured at 800 °C and 1000 °C. Herein, we report a new ternary phase, termed Ni2AlLa, confirmed at 800 °C. Its X-ray diffraction (XRD) pattern was indexed and space group determined using Total Pattern Solution (TOPAS), and the suitable lattice parameters were fitted using the Pawley method and selected-area electron diffraction. Ni2AlLa crystallizes in the trigonal system with a space group R3 (no. 146), a = 4.1985 Å and c = 13.6626 Å. A self-consistent set of thermodynamic parameters for the Al–La and Ni–La binary systems and the Ni–Al–La ternary system includes a Ni2AlLa ternary phase, which was optimized using the CALPHAD method. The calculated thermodynamic and phase-equilibria data for the binary and ternary systems are consistent with the literature and measured data.
More Information
Statistics
Downloads
Share
Actions (login required)
![]() |
View Item |