DINSLEY, Christopher Paul. (2004). Fatigue properties of dissimilar metal laser welded lap joints. Doctoral, Sheffield Hallam University (United Kingdom)..
|
PDF (Version of Record)
10694442.pdf - Accepted Version All rights reserved. Download (66MB) | Preview |
Abstract
This work involves laser welding austenitic and duplex stainless steel to zinc-coated mild steel, more specifically 1.2mm V1437, which is a Volvo Truck Coiporation rephosphorised mild steel. The work investigates both tensile and lap shear properties of similar and dissimilar metal laser welded butt and lap joints, with the majority of the investigation concentrating on the fatigue properties of dissimilar metal laser welded lap joints. The problems encountered when laser welding zinc-coated steel are addressed and overcome with regard to dissimilar metal lap joints with stainless steel. The result being the production of a set of guidelines for laser welding stainless steel to zinc-coated mild steel. The stages of laser welded lap joint fatigue life are defined and the factors affecting dissimilar metal laser welded lap joint fatigue properties are analysed and determined; the findings suggesting that dissimilar metal lap joint fatigue properties are primarily controlled by the local stress at the internal lap face and the early crack growth rate of the material at the internal lap face. The lap joint rotation, in turn, is controlled by sheet thickness, weld width and interfacial gap. Laser welded lap joint fatigue properties are found to be independent of base material properties, allowing dissimilar metal lap joints to be produced without fatigue failure occurring preferentially in the weaker parent material, irrespective of large base material property differences. The effects of Marangoni flow on the compositions of the laser weld beads are experimentally characterised. The results providing definite proof of the stirring mechanism within the weld pool through the use of speeds maps for chromium and nickel. Keywords: Laser welding, dissimilar metal, Zinc-coated mild steel, Austenitic stainless steel, Duplex stainless steel, Fatigue, Lap joint rotation, Automotive.
| Item Type: | Thesis (Doctoral) |
|---|---|
| Contributors: | Thesis advisor - Nordberg, Hans Thesis advisor - Smith, Alan |
| Additional Information: | Thesis (Ph.D.)--Sheffield Hallam University (United Kingdom), 2004. |
| Research Institute, Centre or Group - Does NOT include content added after October 2018: | Sheffield Hallam Doctoral Theses |
| Depositing User: | EPrints Services |
| Date Deposited: | 10 Apr 2018 17:19 |
| Last Modified: | 26 Apr 2021 11:41 |
| URI: | https://shura.shu.ac.uk/id/eprint/19561 |
Actions (login required)
 |
View Item |
Downloads
Downloads per month over past year