BARRAS, Joshua (2023). Investigation of induction-assisted laser metal deposition of crack susceptible coatings. Masters, Sheffield Hallam University.
Documents
33402:639342
PDF
Barras_2024_MPhil_InvestigationOfInduction.pdf - Accepted Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.
Barras_2024_MPhil_InvestigationOfInduction.pdf - Accepted Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.
Download (37MB) | Preview
Abstract
Protecting components against severe wear and corrosion in high temperature environments is an
ongoing challenge that is often resolved by applying an advanced functional coating. Environments
like steam turbines present ever-evolving demands with industrial push to utilise higher operating
temperatures that in turn increase power generation efficiencies.
Tribaloy T800 is a superior coating composition that presents challenges in processability due to its
low toughness and crack susceptible nature. Weld overlay/ cladding processes based on fusion
technology such as Laser Metal Deposition (LMD) (AKA Laser Cladding) offer significant benefits for
the application of coating materials including a high strength metallurgical bond and a dense, defect
free coating. LMD generates more rapid melting and solidification of the alloy compared to arc
cladding, which produces a fine microstructure, but can lead to solidification cracking due to induced
thermal stresses during the process and a lack of toughness in the coating material.
A small number of papers and published research projects have looked into LMD coatings of Tribaloy
T800 with the ultimate aim to prove the feasibility of protecting components in high-temperature
(600-1000°C) gas turbines, jet engines, shafts and pumps. Many of these studies conclude the findings
of process optimisation, material characteristics and integrity, based on small-scale deposits. Small
area deposits can present a lack of representation compared to full-scale coatings, including thermal
control/accuracy, residual stresses, and even effects on dilution. In all circumstances, preheating was
found to reduce or eliminate cracking by minimising the thermal shock and cooling rate of the alloy
upon solidification.
In this study, part of the objectives was to review and ensure the relevance of the experiments and
findings for transferability to full-scale components. Using Design of Experiments (DoE), experiments
were constructed that evaluated the relationship between dilution, hardness and cracking response
of the LMD deposited T800 against critical process variables including particularly induction heating
temperature. One substrate alloy was investigated, 316L stainless steel, (although there was an
intention to transfer developments to In718 nickel superalloy at a later stage). Through this process,
it was determined that cracks form during solidification of the meltpool.
Another objective was to evaluate two methods of improving coatings speeds for the application of
T800, 1) by implementing equipment adaptions to increase melt pool size and material feed rate and
2) to make initial assessment of a novel LMD technique known as Extreme High-speed Laser
Application (EHLA).
Cracking was only eliminated in the large-scale undiluted coatings of T800 when using high levels of
substrate heating (800-950°C) prior and during the coating operation by induction-assisted LMD. The
resultant material behaviour of the deposited T800 showed promising results in terms of material
integrity, and tribological and protective properties. Improvements in coating speeds were made
when using laser defocus methods and increased deposition rate from 300 grams/hour to 600-
1000grams/hour, though increased cracking was observed.
Trials using EHLA demonstrated unique process characteristics of high-speed thin coatings with
promising cracking behaviour at lower preheat temperatures than required for LMD (200-500°C),
ultra-low dilution and good material properties.