Ultrahigh energy density in short-range tilted NBT-based lead-free multilayer ceramic capacitors by nanodomain percolation

Tools

JI, Hongfen, WANG, Dawei, BAO, Weichao, LU, Zhilun, WANG, Ge, YANG, Huijing, MOSTAED, Ali, LI, Linhao, FETEIRA, Antonio, SUN, Shikuan, XU, Fangfang, LI, Dejun, MA, Chao-Jie, LIU, Shu-Yu and REANEY, Ian (2021). Ultrahigh energy density in short-range tilted NBT-based lead-free multilayer ceramic capacitors by nanodomain percolation. Energy Storage Materials. [Article]

[+][-]

Documents

28030:566250
28030:566251

[+][-]

28030:566250

[thumbnail of ENSM-D-20-02047__accepted_version.pdf]

Preview

PDF
ENSM-D-20-02047__accepted_version.pdf - Accepted Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (1MB) | Preview

28030:566251

[thumbnail of NBT-SBT-BMN-supplementary information-2020-11-11.pdf]

Preview

PDF
NBT-SBT-BMN-supplementary information-2020-11-11.pdf - Supplemental Material
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (1MB) | Preview

Abstract

Dense pseudocubic 0.62Na0.5Bi0.5TiO3-0.3Sr0.7Bi0.2TiO3-0.08BiMg2/3Nb1/3O3 (NBT-SBT0.08BMN) ceramics with excellent recoverable energy density, Wrec = 7.5 J/cm3 , and conversion efficiency, η = 92%, were synthesized. Large electric breakdown strength was facilitated by electrical homogeneity, high resistivity and large activation energy (1.86 eV). Transmission electron microscopy identified the presence of polar nano-regions (PNRs) in a matrix of short coherence in-phase and antiphase octahedral tilting. Combining polar and tilt order restricted the crystal classes of PNRs to tetragonal, orthorhombic and monoclinic. Using these symmetries, the enhancement of polarization was explained using Landau-Devonshire phenomenology and percolation theory. Octahedral tilting and introduction of larger B-site ions (Mg2+, Nb5+) inhibited long range polar coupling, minimizing strain and maximizing η. Wrec was further improved to 18 J/cm3 (>1000 kV/cm) in multilayers whose properties were stable from 0.01–100 Hz, from 20 °C–160 °C and up to 106 cycles, attractive for pulsed power applications and power electronics.

More Information

Official URL:

https://www.sciencedirect.com/science/article/pii/...

Uncontrolled Keywords:

0904 Chemical Engineering; 0906 Electrical and Electronic Engineering

Identifiers

Identification Number:

10.1016/j.ensm.2021.01.023

ORCID for Antonio Feteira: