LI, Ao, HU, Yanhong, LIU, Zhaogang, ZHANG, Xiaowei, DENG, Wei, WANG, Hongyuan, LI, Mei and WANG, Mitang (2019). The effect of mixed La-Y doping on water resistance of phosphate glass. Journal of Non-Crystalline Solids, 527, p. 119727.

The effect of mixed La-Y doping on water resistance of phosphate.pdf - Accepted Version
Creative Commons Attribution Non-commercial No Derivatives.

Download (754kB) | Preview
Official URL:
Link to published version::


In this work, the effect of mixed La-Y doping on the water resistance of xLa2O3–(16-x)Y2O3–8Al2O3–10Na2O–66P2O5 (x = 0, 4, 8, 12, 16 mol%) glasses was studied. The glass structure, glass transition temperature (Tg), dc conductivity (σdc) and water resistance of glass were respectively characterized by Fourier transform infrared spectroscopy (FTIR), differential scanning calorimeter (DSC), electrochemical workstation and water resistance test. The results show that with the gradual replacement of Y2O3 by La2O3, the value of Q(2) (Q2 content as a percentage of the sum of Q1 and Q2 contents in glass structure) and water resistance characterized by mass loss per unit surface area indicate strong “mixed rare earth effect”. It is obvious that the change of glass structure causes water resistance of glass to vary nonlinearly and exhibit a positive deviation from linearity. The results can provide some useful information for tailoring the chemical durability of glass by mixed rare earth doping.

Item Type: Article
Uncontrolled Keywords: 0912 Materials Engineering; Applied Physics
Identification Number:
Page Range: p. 119727
SWORD Depositor: Symplectic Elements
Depositing User: Symplectic Elements
Date Deposited: 04 Nov 2019 16:41
Last Modified: 17 Mar 2021 21:02

Actions (login required)

View Item View Item


Downloads per month over past year

View more statistics