Temperature Stable and Fatigue Resistant lead-free ceramics for actuators

Lead-free ceramics with the composition 0.91K1/2Bi1/2TiO3–0.09(0.82BiFeO3-0.15NdFeO3-0.03Nd2/3TiO3) were prepared using a conventional solid state, mixed oxide route. The ceramics exhibited a high strain of 0.16% at 6 kV mm1, stable from room temperature to 175 C, with a variation of <10%. The materials were fabricated into multilayer structures by co-firing with Pt internal electrodes. The prototype multilayer actuator exhibited constant strains up to 300 C with a variation of 15%. The composition showed fatigue resistant behaviour in both monolithic and multilayer form after bipolar loading of 106 cycles.