Fabrication and characterization of textured Bi2Te3 thermoelectric thin films prepared on glass substrates at room temperature using pulsed laser deposition

YU, Z., WANG, X., DU, Y., AMINORROAYA YAMINI, Sima, ZHANG, C., CHUANG, K. and LI, S. (2013). Fabrication and characterization of textured Bi2Te3 thermoelectric thin films prepared on glass substrates at room temperature using pulsed laser deposition. Journal of Crystal Growth, 362 (1), 247-251.

Full text not available from this repository.
Official URL: http://www.sciencedirect.com/science/article/pii/S...
Link to published version:: https://doi.org/10.1016/j.jcrysgro.2012.05.045

Abstract

Thin films of n-type Bi2Te3 were fabricated on glass substrates at room temperature using pulsed laser deposition. Samples were characterized by using X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectroscopy, and a physical properties measurement system. The XRD and Raman results show that crystalline films can be easily achieved at room temperature, and all films have a preferred crystal growth texture along the (0 1 5) direction. SEM indicates that the films are high-quality and smooth. The Seebeck coefficient, electrical resistivity, and magnetoresistance were measured over wide ranges of temperature and magnetic field. It was found that Seebeck coefficient of the films was significantly enhanced after annealing process.

Item Type: Article
Research Institute, Centre or Group - Does NOT include content added after October 2018: Materials and Engineering Research Institute > Engineering Research
Identification Number: https://doi.org/10.1016/j.jcrysgro.2012.05.045
Page Range: 247-251
Depositing User: Sima Aminorroaya Yamini
Date Deposited: 25 Jul 2017 14:00
Last Modified: 18 Mar 2021 11:15
URI: https://shura.shu.ac.uk/id/eprint/15956

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics